中國閥門、日本閥門、德國閥門、英國閥門、美國閥門及閥門標(biāo)準(zhǔn)規(guī)定的常用金屬材料對照表
分
類 | 序
號 | 中國 | 日本 | 標(biāo)準(zhǔn) | 美國 | 英國 | 德國 |
GB1220
GB1221
GB12228
GB12229
Gb12230 | JIS | ISO683/13
ISO683/16 | ANSI
ASTM | Bs970
Bs1449 | DIN17440
DIN17224 |
鑄
碳
素
鋼
合
金
鋼 | 1 | WCA | G5151 SCPH1 | | A216 WCA | 161Cr-430F | GS-C25 |
2 | ZG230-450 WCB | G5151 SCPH2 SC410 | | A216 WCB | | |
3 | WCC | | | A216 WCC | | |
4 | ZG20CrMo | | | A217 Wc5 | 3100 B2 | |
5 | | G5151 SCPH21 | | A217 Wc4 | 1504 621E | |
6 | ZG15CrMoV | | | | 3100 B3 | |
鑄
不
銹
鋼 | 7 | ZG00Cr18Ni10 | G5121 SCS19A | | A351 CF3 | 1504 304C12E | |
8 | ZGOCr18Ni9Ti | G5121 SCS13A | | A351 CF8 | 1504 304C15E | G-X6CrNiMo1810 |
9 | CF3M | G5121 SCS16A | | A351 CF3M | 1504 316C12E | |
10 | ZGOCr18Ni12Mo2Ti | G5121 SCS14A | | A351 CF8M | 1504 316C16E | |
11 | CF8M | G5121 SCS14A | | A744 CF-8M | 3100 316C16 | |
12 | CF8C | G5121 SCS21 | | A351 CF8C | 1504 347C17E | G-X7CrNiNb1189 |
13 | CF8 | G5121 SCS13A
G5121 SCS13 | | A744 CF-8 | 3100 304C15 | G-X6CrNi189 |
14 | CF3 | G5121 SCS19A | | A744 CF-3 | 3100 304C12 | |
鍛
不
銹
鋼 | 15 | ZGOCr17Ni4Cu4Nb | G5121 SCS24 | | 17-4PH | | |
16 | 1Cr18Ni9 | SUS302 | 12 | 302,S30200 | 302S25 | X12CrNi188 |
17 | 0Cr18Ni9 | SUS304 | 11 | 304,S3400 | 304S15 | X5CrNi189 |
18 | 00Cr18Ni10 | SUS304L | 10 | 304L,S30403 | 304S12 | X2CrNi189 |
19 | 0Cr25Ni20 | SUS310S | | 310S,S31008 | | |
20 | 0Cr17Ni12Mo2 | SUS316 | 20,20 | 316,S31600 | 316S16 | X5CrNiMo1810 |
21 | 1Cr18Ni12Mo2Ti | | | | 320S17 | X10CrNiMoTi1810 |
22 | 0Cr18Ni12Mo2Ti | | | | 320S17 | X10CrNiMoTi1810 |
23 | 00Cr17Ni14Mo2 | SUS316L | 19,19 | 316L,S31603 | 320S12 | X2CrNiMo1810 |
24 | 0Cr17Ni12Mo2N | SUS316N | | 316N,S31651 | | |
25 | 0Cr17Ni4Cu4Nb | | | 17-4PH | | X2CrNiMoN1812 |
26 | 0Cr17Ni13Mo2N | SUS316LN | | | | |
27 | 0Cr18Ni12Mo2Cu2 | SUS316J1 | | | | X10CrNiTi189 |
28 | 1Cr18Ni9Ti | | | | | X10CrNiTi189 |
29 | 0Cr18Ni10Ti | SUS321 | 15 | 321,S32100 | 321S21，321S20 | |
30 | 1Cr13 | SUS410 | 3 | 410,S41000 | 410S21 | X10Cr13 |
31 | 0Cr13 | SUS410S | 1 | 410S | 403S17 | X7Cr13 |
32 | 2Cr13 | SUS420J1 | 4 | 420S,S42000 | 420S37 | X20Cr13 |
33 | 3Cr13 | SUS420J2 | 5 | 420S45 | | |
34 | 4Cr13 | SUS420J2 | 5 | 431,S43100 | 431S29 | X22CrNi17 |
35 | 0Cr17Ni14Cu4Nb | SUS630B | | 630,S17400 | | X7CrNiA1177 |
36 | 00Cr25Ni20Mn3Mo3N | | | | U3 | |
37 | 0Cr17Mn14Mo2N | | | A4 | | |
38 | 00Cr20Ni25Mo4Cu2 | | 904L | | UB6 | |
39 | 00Cr15Ni60M16W4 | | | （哈氏C） | | |
40 | 0Cr20Ni30Mo2Cu3 | | (20號合金) | | | |
41 | 0Ni70Cu30Mn | | （蒙耐爾） | | | |
閥體材料：WCB碳鋼。WCB相當(dāng)于25或35碳鋼，我在某些不知道是不是正確的資料上說是：W代表焊接， C代表鑄造，zui后一個字母代表閥體鋼的型號。如果照一樓如此說的話，應(yīng)該是屬于特殊材料的代號。
鑄造時可以使用WCA、WCB、WCC等代號，分別代表ZG205-415、ZG250-485、ZG275-485